Abstract
Abstract The effect of laser shock processing (LSP) on the hardness, surface morphology, residual stress, and thermal fatigue properties of a ZCuAl10Fe3Mn2 alloy was investigated to improve the thermal fatigue performance and decrease the surface crack of high-temperature components. The microstructure and crack morphology were analyzed by scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS). The results showed that laser shock could significantly improve the thermal fatigue performance of the alloy at a pulse energy of 4 J. Under the effect of thermal stress and alternating stress, microstructure around the specimen notch was oxidized and became porous, leading to the formation of multiple micro-cracks. The micro-cracks in the vertical direction became the main cracks, which mainly expanded with the conjoining of contiguous voids at the crack tip front. Micro-cracks in other directions grew along the grain boundaries and led to material shedding.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Transactions of Nonferrous Metals Society of China
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.