Abstract
The effect of single and two-stage Si modified aluminide coatings on thermal fatigue behaviour of nickel based superalloy Inconel 713LC was examined. Specimens were loaded under test condition of heating to 1100°C followed by cooling to25°C. The experimental results showed that the coatings increased thermal fatigue resistance in both crack initiation and propagation stages. The comparison of the crack growth rates indicated that both coatings imparted resistance to the crack lengthening. However, the effect of single stage coating on the fatigue resistance was superior compared with that of two-stage coating. Through scanning electron microscopy observation, it was found that the width of γ′ denuded zone was the main reason in the control of crack growth in all specimens.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.