Abstract
High-temperature thermal fatigue causes the failure of thermal barrier coating (TBC) systems. This paper addresses the development of thick TBCs, focusing on the microstructure and the porosity of the yttria partially stabilized zirconia (YPSZ) coating, regarding its resistance to thermal fatigue. Thick TBCs, with different porosity levels, were produced by means of a CoNiCrAlY bond coat and YPSZ top coat, both had been sprayed by air plasma spray. The thermal fatigue resistance of new TBC systems and the evolution of the coatings before and after thermal cycling was then evaluated. The limit of thermal fatigue resistance increases depending on the amount of porosity in the top coat. Raman analysis shows that the compressive in-plane stress increases in the TBC systems after thermal cycling, nevertheless the increasing rate has a trend which is contrary to the porosity level of top coat.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.