Abstract
AbstractThe high-temperature (HT) behaviour of a sample of natural alunite was investigated by means of in situ HT single-crystal X-ray diffraction from room temperature up to the dehydroxylation temperature and consequent collapse of the crystal structure. In the temperature range 25–500°C, alunite expands anisotropically, with most of the contribution to volume dilatation being produced by expansion in the c direction. The thermal expansion coefficients determined over the temperature range investigated are: αa = 0.61(2) × 10–5 K–1 (R2 = 0.988), αc = 4.20(7) × 10–5 K–1 (R2 = 0.996), αc/αa = 6.89, αV = 5.45(7) × 10–5 K–1 (R2 = 0.998). At ∼275–300°C, a minor discontinuity in the variation of unit-cell parameters with temperature is observed and interpreted on the basis of loss of H3O+ that partially substitutes for K+ at the monovalent A site in the alunite structure. Increasing temperature causes the Al(O,OH)6 sheets, which remain almost unaltered along the basal plane, to move further apart, and this results in an expansion of the coordination polyhedron around the intercalated potassium cation. Sulfate tetrahedra act as nearly rigid units, they contract a little in the lower temperature range to accommodate the elongation of the Al octahedra.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.