Abstract
Polycarbonate nanocomposites filled with pristine and modified silica were prepared by simple melt compounding. The thermal degradation behavior of composites was investigated by thermogravimetric analysis coupled with differential scanning calorimetry (TGA/DSC). To understand the thermal degradation mechanism, the chemical structures of gaseous and solid degradation products were detected by thermogravimetric analysis coupled with Fourier transform infrared spectrometry (TGA/FTIR) and X-ray photoelectron spectroscopy (XPS), respectively. Kissinger–Akahira–Sunose (KAS) and Flynn–Wall–Ozawa (FWO) methods were employed to analyze the thermal degradation kinetics. High thermal degradation temperature was obtained by incorporating both types of nanoparticles into matrix, but the maximum mass loss rate increased. According to the DSC curves for degradation process, the change of the number and position of absorption peaks meant that the degradation mechanism of composites was different from that of neat PC. The analysis for TGA chars confirmed the presence of alcoholysis reaction between PC and silica nanoparticles during the thermal decomposition. TGA/FTIR results proved that no new degradation volatiles were produced during the thermal degradation of composites, but the total amounts of all gaseous products decreased by adding silica nanoparticles. The degradation activation energies of both composites increased significantly relative to neat PC, especially for the composite with modified silica.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.