Abstract
SummaryPlantation Chinese fir wood was modified by low molecular weight phenol melamine urea formaldehyde (PMUF) resin, boron compounds (BB), and the mixture of PMUF/BB (PMUF‐BB), followed by a curing step. The fire performance and thermal degradation of wood was measured by limiting oxygen index instrument, cone calorimeter, and simultaneous thermal analysis. The results showed that the limiting oxygen index increased to 50.7%, 43.5%, and 55.0% for BB, PMUF, and PMUF‐BB samples, respectively. The PMUF resin decreased the heat release rate of wood but increased the total heat release compared with the control samples. The thermal analysis results demonstrated that PMUF resin enhanced the thermal stability of wood, however, had little impact on the residual chars. Combinative treatment with boron compounds could substantially reduce the fire risk for PMUF‐modified wood, making them especially useful for application in public settings.
Submitted Version
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.