Abstract

ABSTRACT Epoxy/graphite/expanded graphite composites have been prepared in various weight ratios and thermal degradation and electrical properties were estimated in order to use for the bipolar plate materials in PEMFC. Thermogravimetric analysis (TGA) showed that the epoxy/graphite system cured by a curing agent GX-533 was most proper because its weight loss until 80℃ at which PEMFC would be operated was 0.3 wt%, and differential scanning calorimetry (DSC) analysis showed its cure temperature would be sufficient at 80℃. The activation energy for the cure reaction was 132.0 kJ/mol and the pre-exponential factor was 1.76×10 17 min -1 . Electrical conductivity on the surface of the bipolar plate prepared under a pressure of 200 kgf/cm 2 was increased from 4 to 25 S/cm 2 by increasing expanded graphite (EG) content from 50 phr to 90 phr. The percolation threshold was initiated around 75 phr and the corrosion rate at 80 phr was 1.903 uA/cm 2 .KEY WORDS :PEMFC( 고분자 전해질 연료전지), Bipolar plate(바이폴라 플레이트), Composite(복합재료), Epoxy resin(에폭시 수지), Expanded graphite(팽창 흑연)

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.