Abstract
The main modifications of thermal and colorimetric parameters after thermal aging of DGEBA/TETA system (plain epoxy) and fique-fiber woven fabric-reinforced epoxy composites are described. As a preliminary study, thermal analysis was carried out on epoxy matrix composites reinforced with 15, 30, 40 and 50% fique-fiber woven fabric. After this previous analysis, the 40% composite was chosen to be thermally aged, at 170 °C. Three exposure times were considered, namely, 0, 72, 120 and 240 h. Samples were studied by thermogravimetric analysis (TGA), differential thermal analysis (DTA), differential scanning calorimetry (DSC), thermomechanical analysis (TMA) and colorimetry analysis. Significant color changes were observed after thermal aging combined with oxidation. It was also found that the thermal behavior of the plain epoxy showed greater resistance after thermal exposure. By contrast, the composites were more sensitive to temperature variations as a result of thermal stresses induced between fique fibers and the epoxy matrix.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.