Abstract
A study was undertaken on a Ti–25Nb–3Mo–3Zr–2Sn alloy using differential scanning calorimetry (DSC) in order to improve understanding of the precipitation reactions occurring during aging heat treatments. The investigation showed that isothermal ω phase can be formed in the cast and solution treated alloy at low aging temperatures. An exothermic peak in the temperature range of 300 to 400°C was detected for precipitation of the ω phase, with approximate activation energy of 176 kJ/mol. The ω phase begins to dissolve at temperatures around 400°C and precipitation of the α phase is favoured at higher temperatures between 400°C and 600°C. An exothermic peak with activation energy of 197 kJ/mol was measured for precipitation of the α phase. Deformation resulting in the formation of the stress induced α″ phase altered the DSC heating profile for the solution treated alloy. The exothermic peak associated with precipitation of the ω phase was not detected during heating of the deformed material and increased endothermic heating associated with recovery and recrystallisation was observed.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have