Theoretical Evaluation of Crosslink Density of Chain Extended Polyurethane Networks Based on Hydroxyl Terminated Polybutadiene and Butanediol and Comparison with Experimental Data

Abstract

ABSTRACTPolyurethane networks between hydroxyl terminated polybutadiene (HTPB) and butanediol (BD) were prepared using toluene diisocyanate (TDI) as the curative. HTPB and BD were taken at equivalent ratios viz.: 1:0, 1:1, 1:2, 1:4, and 1:8. Crosslink density (CLD) was theoretically calculated using α-model equations developed by Marsh. CLD for the polyurethane networks was experimentally evaluated from equilibrium swell and stress–strain data. Young’s modulus and Mooney–Rivlin approaches were adopted to calculate CLD from stress–strain data. Experimentally obtained CLD values were enormously higher than theoretical values especially at higher BD/HTPB equivalent ratios. The difference in the theoretical and experimental values for CLD was explained in terms of local crystallization due to the formation of hard segments and hydrogen bonded interactions.