Abstract
AbstractThe paper has presented the results of theoretical studies and experimental tests of the plastic deformation of Mg/Al bimetallic specimens. Theoretical studies were carried out using the Forge2011® computer program. Physical modeling, on the other hand, was performed using the Gleeble3800 simulator. Bimetallic bars of an outer diameter of 22.5 mm and a cladding layer thickness of 1.7 mm were obtained by the explosive welding method. Samples for formability tests, characterized by a diameter-to-length ratio of 1, were taken from the bars. The theoretical studies and experimental tests were carried out for the temperature range from 300 to 400°C and for different strain rates. Based on the obtained investigation results it has been found that the main parameters influencing the formability of Mg/Al bimetallic bars are strain rate than the process temperature.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.