Abstract
The experimental densification kinetics of 7.8 mol% Y2O3-stabilized zirconia was analyzed theoretically during isothermal sintering in the final stage. By taking concurrent grain growth into account, a possible value of the grain-size exponent n was examined. The Coble’s corner-pore model recognized widely was found not to be applicable for explaining the densification kinetics. The corner-pore model of n = 4 shows a significant divergence in the kinetics at different temperatures. Microstructural observation shows that most pores are not located at grain corners and have a size comparable to the surrounding grains. The observed pore structure is similar to the diffusive model where single pore is surrounded by dense body. The diffusive model combined with theoretical sintering stress predicts n = 1 or n = 2, which shows a good consistence to the measured densification kinetics. During sintering of nano-sized powder, it is found that the densification kinetics can be explained distinctively by the diffusive single-pore model.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.