The wear characteristics of ultrahigh molecular weight polyethylene against a high density alumina ceramic under wet (distilled water) and dry conditions

Abstract

In recent years there has been growing interest in the use of high density alumina ceramic material for the femoral ball in association with ultrahigh molecular weight polyethylene (UHMWPE) for the acetabular component in total replacement hip joints. The wear characteristics of UHMWPE pins sliding against a high density alumina ceramic disc in the presence of distilled water in a tri-pin-on-disc machine have been revealed in very long-term experiments reported in this paper. A total sliding distance in excess of 6000 km was achieved and very low mean wear coefficients of the order of 10 −8 mm 3 N −1 m −1 were recorded. Experiments were also carried out over a shorter sliding distance under dry conditions and the average wear coefficient of 2 × 10 −7 mm 3 N −1 m −1 was consistent with earlier findings. In these dry tests, comet-like streaks of polyethylene were transferred to the ceramic counterface, but no such transfer was noted during the wet tests. When distilled water was added to the test chamber after a considerable period of dry sliding, the wear coefficient rapidly decreased to about 10 −8 mm 3 N −1 m −1 and the streaky transfer film disappeared from the ceramic counterface. The possibility of hydrodynamic action between the wear face on the pins and the counterface was investigated by reversing the direction of sliding. Surface topography changes on both the pins and the discs and friction and bulk temperatures of the pins were recorded throughout the tests. It is concluded that the excellent dry wear coefficients of UHMWPE sliding on alumina ceramic counterfaces are about twenty times greater than those experienced by the same materials in the presence of distilled water. The tribological advantage of the ceramic with respect to stainless steel having a similar surface roughness has been confirmed in dry sliding involving UHMWPE, but further work is required to determine whether or not the same advantage can be achieved under wet conditions.