Abstract
The use of more economical quasi-static testing to predict the dynamic impact behaviour of marine GRP composites has been evaluated by comparing equivalent impact and quasi-static test results. Static tests predicted well the initial impact behaviour and onset of delamination damage, which is likely to be the key impact resistance design variable. However, only very conservative estimates of the final fibre failure and total energy absorption capacity were achieved, except for the thickest specimens where fibre damage occurred at similar loads for both static and impact tests. Quasi-static testing avoided the problems associated with oscillations in the force signal, and delamination force showed a very strong linear relationship with laminate thickness3/2 as predicted by two simplified models. It was inferred that the undamaged and delaminated responses are not strain rate dependant, but that the fibre failure mechanisms are.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.