Abstract
Porous polymer films and plasticised polymer films of vinylidene fluoride (VDF)–hexafluoropropylene (HFP)–chlorotrifluoroethylene (CTFE) terpolymers have been fabricated from a range of solvents. Significant 2EC/PC solvent uptake was measured at 60 °C for VDF–HFP–CTFE terpolymer films but structural integrity was maintained. 0.625 Ah soft packaged graphite—LiCoO 2 test cells have been fabricated containing porous VDF–HFP–CTFE terpolymer films as separator. Ninety-eight percent of Rated Capacity was measured at 2 C rate. Four hundred and fifty-four cycles were obtained at C rate to 80% of Rated Capacity. Thin 4–5 μm plasticised VDF–HFP–CTFE terpolymer films have also been produced.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.