Abstract
Samples of Ho3+/Yb3+ codoped ZrO2-ZnO powder were prepared by a solid-state reaction. Upconversion luminescence of Ho3+ /Yb3+ codoped ZrO2-ZnO powders was reported in the present paper. The excitation spectrum detected at room temperature suggests three excitation peaks centered at 540, 671 and 762 nm respectively, corresponding to 5S2/5F4 --> I8, 5 Fs --> 5 I8, and 5S2/5 F4 --> 5 I7 or 5 I4 --> 5 I8 of Ho3+ ions. The contents of rare-earth ions could influence the property of upconversion lumunescence. When the Ho3+ content was 0.1 mol%, with the increase in Yb3+ content, the intensity of red luminescence and green luminescence decreased first and then increased, but the intensity of infrared luminescence increased first and then decreased. Furthermore, the ratio of the intensity of green emission to red emission decreased. When the Yb3+ content was 4.7 mol%, with the increase in Ho3+ content, the intensity of all emission decreased, but the ratio of the intensity of green emission to red emission was almost constant. The logI - logP curve shows that all the upconversion luminescence is double-photon processes. And the upconversion mechanisms of the samples were introduced. It is shown from the XRD spectrum that the powder of samples is uniform.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.