Abstract
The quenching and partitioning (Q&P) process is a heat treatment process, aiming at the creation of steel microstructures composed of martensite and retained austenite. Herein, the thermal stability of the microstructure is investigated upon reheating steel microstructures, created with different Q&P settings, in different thermal routes, using dilatometry and thermomagnetometry to quantitatively monitor phase fractions. Analysis of the derivative of dilatometry curves and thermomagnetic data reveals that upon reheating the retained austenite decomposes. The decomposition occurs in two stages when the heating rate is relatively low. The retained austenite completely transforms to ferrite and cementite upon reheating to 550 °C, followed by isothermal holding for 1800 s. Increasing the partitioning time from 50 to 300 s at 400 °C after quenching to 260 °C significantly increases the thermal stability of retained austenite. In all conditions, both carbon‐depleted martensite (formed in the initial quenching step) and fresh martensite (formed in final Q&P quenching) are found to be partially tempered during the reheating experiments.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.