Abstract
The crystal of p-aminohippuric acid was polymerized in the solid state by annealing at a temperature below its melting point. The reaction was carried out on the p-aminohippuric acid crystal at 170°C for 260 h under reduced pressure. The specimens formed through the thermal solid state polycondensation procedure from original monomer single crystals were examined mainly by means of differential thermal analysis (DTA), X-ray diffractometry and scanning electron microscopic (SEM) observation. In DTA measurements, whereas the endothermic spike peak of a monomer single crystal was observed approximately at 200 °C, the endothermic peak of a polymerized specimen appeared approximately at 380°C
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.