The tensile properties of an Fe-4 pct Mo-0.2 pct C martensite tempered under applied stress

Abstract

In Fe-4 pct Mo-0.2 pct C martensite which is a typical secondary hardening steel, premature failure o°Curred in tensile test at 600 °C to 700°C where solute atoms could diffuse easily. To clarify this phenomenon, the quenched specimens were tempered under applied stress and tensile-tested at room temperature. The following results were obtained: (1) Typical intergranular fracture was observed in specimens tempered in a temperature range of 600 °C to 650 °C with tempering times of five minutes to 10 minutes and applied stress (70 MPa to 140 MPa). (2) Based on Auger analysis, this phenomenon was considered to be caused by segregation of P, S, and Mo on prior austenite grain boundaries due to applied stress. (3) The direction of applied stress was found to be very significant. Namely, when the tensile direction was parallel to the applied stress during tempering, the specimen was more brittle, and when tensile direction was normal to the applied stress, the specimen was not so brittle. (4) To reduce this embrittlement, solution treatment temperature was adjusted, and it was found that the embrittlement was considerably reduced both in specimens with fine prior austenite grains and with some ferrite phase on prior austenite grain boundaries.