Abstract
AbstractTo enhance the fracture toughness of epoxy resin at low temperature, a secondary branched epoxy‐terminated silicone resin (ESR‐6) was synthesized and incorporated into bisphenol A epoxy resin at different contents. The structure of ESR‐6 was characterized by Fourier transform infrared spectroscopy and nuclear magnetic resonance (1H NMR), and the fracture surface of the composites was observed by scanning electron microscope (SEM) and atomic force microscopy. At room temperature and − 70°C, the maximum values of elongation at break were 15.78% and 12.55% with 10 wt% ESR. Compared with those of neat epoxy resin, the values of elongation at break of the composite were increased by 50.86% and 36.12%. The results of dynamic mechanical analysis also showed that the toughness of the modified resin had been improved. The SEM images of the fracture surfaces suggested that the fracture mode of the modified resin changed from brittle one to plastic one because of the addition of ESR‐6, which further confirmed the toughening effect of ESR‐6. These research results may provide a new strategy for enhancing the low‐temperature toughness of epoxy resins.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.