Abstract
High-quality P6322 Mn2N0.86 samples were synthesised using a high-pressure metathesis reaction, and the properties of the material were investigated. The measurements revealed that the Vickers hardness was 7.47 GPa, which is less than that predicted by commonly used theoretical models. At low air pressure, Mn2N0.86 and MnO coexist at 500 to 600 °C, and by excluding air, we succeeded in producing Mn4N by heating Mn2N0.86 in nitrogen atmosphere; we carefully studied this process with thermogravimetry and differential scanning calorimetry (TG-DSC). This gives a hint that to control temperature, air pressure and gas concentration might be an effective way to prepare fine Mn-N-O catalysis. Magnetic measurements indicated that ferromagnetism and antiferromagnetism coexist within Mn2N0.86 at room temperature and that these magnetic properties are induced by nitrogen vacancies. Ab intio simulation was used to probe the nature of the magnetism in greater detail. The research contributes to the available data and the understanding of Mn2N0.86 and suggests ways to control the formation of materials based on Mn2N0.86.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.