Abstract
ABSTRACTThe first study of the TiW nitrides (TiWNx) as the Schottky contact metals to the n type Ga0.51In0 49P has been made. The Ga0.51 In0.49P epitaxial layer was successfully grown on the GaAs substrate by LP-MOCVD to form a lattice-matched heterostructure. The RF-magnetron sputtering system was utilized for the nitride deposition. The thermal stability of the nitride films were studied using rapid thermal annealing (RTA) method. Both the electrical characteristics and the materials characteristics were investigated. The materials properties of the nitride films were characterized by X-ray diffraction (XRD), Transmission electron microscopy (TEM), and Auger electron spectroscopy (AES). The TiWNx Schottky contacts demonstrate excellent electrical and physical characteristics, even after high temperature annealing. The barrier heights range from 0.81 to 1.05 eV depending on the content of the nitrogen and the annealing conditions. The XRD and AES results show no indication of interaction at the TiWNX/GaInP interface of both as-deposited and annealed samples. The outstanding characteristics of the contact were attributed to the high bandgap nature of the Ga0.51In0.49P and the incorporation of nitrogen into the TiW films.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.