Abstract
This present study shows, the effect of applying pressure at rang(10-84) MPa using squeeze casting process to improve the microstructure and actual density of Aluminum alloy A380 was studied.From fig(5) its clear that the microstructure of prepare casting samples consists of two phases of hard eutectic (Al-Si) and Primary α-Al. The effect of applying pressure leads to increase the surface fraction percentage of eutectic phase at (68-84) MPa, but the eutectic percentage was decreased at the same range the actual density was increased at (10,17,84) MP.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.