Abstract

AbstractSummary: The structure of the free volume and its temperature dependence between 25 and 190 °C of copolymers of styrene with acrylonitrile, SAN (0 to 50 mol‐% AN), is studied by pressure volume temperature (PVT) experiments and positron annihilation lifetime spectroscopy (PALS). In this second part of the work, PALS data are reported from which the temperature dependence of the mean size and size distribution of local free volumes (subnanometer size holes) is analysed. The mean hole volume, vh, varies in PS between 105 Å3 (27 °C) and 220 Å3 (190 °C), and shows a systematic decrease with increasing AN content, at Tg from 121 Å3 for PS to 102 (±2) Å3 for SAN50. The specific number of holes, $N_{\rm h} '$, estimated from a comparison of PVT and PALS results, is independent on the temperature and the composition of SAN, $N_{\rm h} '$ = (0.56 ± 0.02) × 1021 g−1 which corresponds to Nh(Tg) = $N_{\rm h} '$/V(Tg) = 0.59 nm−3 and 1/Nh(Tg) = 1.7 nm3 for the volume which contains one hole. The analysed size distributions of the holes above Tg follow the compressibility of the free volume as it is predicted by the theory of thermal volume fluctuation. Moreover, we showed that the bulk elasticity modulus follows mastercurves as a function of vh above and below Tg.Free volume hole radius distribution n(rh) in PS for three different temperatures.magnified imageFree volume hole radius distribution n(rh) in PS for three different temperatures.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.