Abstract
In the present work, MgAl2-x(Mg0·5Ti0.5)xO4 (x = 0.02, 0.04, 0.06, 0.08, 0.10) solid solutions were synthesized via the traditional solid-state reaction route. The valence state of Ti ions, crystal structural characteristics, and microwave dielectric properties were discussed. A solid solution with spinel structure was revealed by the Rietveld refinement results. The partial substitution of (Mg0·5Ti0.5)3+ for Al3+ lowered the sintering temperature and improved the Q × f value of MgAl2O4 ceramic. The MgAl2-x(Mg0·5Ti0.5)xO4 solid solutions with x = 0.06 can be well sintered at 1425 °C in an oxygen atmosphere for 8 h and exhibits excellent microwave dielectric properties with εr = 9.1, Q × f = 98,000 GHz, τf = −61.36 ppm/°C. The sintering temperature of MgAl1·94(Mg0·5Ti0.5)0.06O4 microwave dielectric ceramics was approximately 200 °C lower than that of conventional MgAl2O4 ceramics.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.