The structure and properties of chromium nitride coatings deposited using dc, pulsed dc and modulated pulse power magnetron sputtering

Abstract

The time averaged ion energy distributions and ion fluxes of continuous dc magnetron sputtering (dcMS), middle frequency pulsed dc magnetron sputtering (PMS), and modulated pulse power (MPP) magnetron sputtering plasmas were compared during sputtering of a Cr target in an Ar/N 2 atmosphere in a closed field unbalanced magnetron sputtering system. The results showed that the dcMS plasma exhibited a low ion energy and ion flux; the PMS plasma generated a moderate ion flux of multiple high ion energy regions; while the MPP plasma exhibited a significantly increased number of target Cr + and gas ions with a low ion energy as compared to the dcMS and PMS plasmas. Cubic CrN coatings were deposited using these three techniques with a floating substrate bias. The structure and properties of the coatings were characterized using X-ray diffraction, scanning electron microscopy, transmission electron microscopy, nanoindentation, microscratch and ball-on-disk wear tests. It was found that the deposition rate of the MPP CrN depositions was slightly lower than those of the dcMS depositions, but higher than in the PMS depositions at similar average target powers. The coatings deposited in the dcMS and PMS conditions without the aid of the substrate bias exhibited large columnar grains with clear grain boundaries. On the other hand, the interruption of the large columnar grain growth accompanied with the renucleation and growth of the grains was revealed in the MPP CrN coatings. The MPP CrN coatings exhibited a dense microstructure, fine grain size and smooth surface with high hardness (24.5 and 26 GPa), improved wear resistance (COF = 0.33 and 0.36) and adhesion, which are the results of the low ion energy and high ion flux bombardment from the MPP plasma.