The structure and optical properties of amorphous thin films along the [formula omitted] - [formula omitted] tie-line prepared by spin-coating

Abstract

The extremely high melting point of Mo, W and their sulfides acts as a barrier to the synthesis of chalcogenide glasses modified with these transition metal elements. Here, we demonstrate the preparation of amorphous thin films along the pseudobinary As40S60 - MoS3 tie-line by spin-coating. Using 0.02 M stock solutions, the limiting As40S60 : MoS3 molar ratio was found to be 1 : 3 for the deposition of highly transparent, very smooth and compact defect-free amorphous thin films. The spectral analysis of optical constants revealed that both the refractive index and extinction coefficient decrease with increasing MoS3 content. On the other hand, the contribution of absorption tails was observed starting from the ratio 2 : 1 and they gradually become more intense and red-shifted with increasing MoS3. Using Raman and infrared spectroscopies (ATR), we confirmed that As40S60 and MoS3 reacted chemically in solution and all thin layers contained only residual amounts of organic ammonium salts after annealing at 200∘C. Our results demonstrate that the sol-gel method can be a feasible and cost-effective strategy for the preparation of amorphous chalcogenide thin films containing transition metals.