The solid film lubrication by carbon ion implantation into α-Al 2O 3

Abstract

Improvement in tribological performance by C +110 keV implantation can be achieved by having a more graphite-like carbon structure on Al 2O 3. It was shown that fracture toughness and critical peeling load increased for a fluence of 5 × 10 17C +/cm 2 because of residual compression stress and amorphism of surface. The testing in a different implantation dose indicated that the friction and wear mechanism in Optimol fretting wear machine (SRV) was a combination of surface structure and its abrasive wear. Raman shift shows that the amorphous graphite with 5 × 10 17–1 × 10 18 C +/cm 2 implantation dose was formed on Al 2O 3 surface, so that it reduced friction coefficient and wear of Al 2O 3, also it is noticed that the failure of lubrication due to graphite-like film wear is much earlier in the implantation sample with 1 × 10 17C +/cm 2 dose.