The Small Fatigue Crack Growth Behavior of an AM60 Magnesium Alloy

Abstract

The effects of thermomechanical processing and subsequent heat treatment on the small fatigue crack growth (FCG) behavior of an AM60 (Mg-6.29Al-0.28Mn wt pct) alloy were evaluated. The effects of mechanical loading parameters, such as maximum stress and load-ratio, on the small FCG behavior were also determined. Maximum stress did not appear to affect the crack propagation rate of small cracks in the stress and crack size ranges considered. Materials with different microstructures and yield stresses, introduced by different processing conditions, showed similar crack growth rates at equivalent stress intensity factor ranges. The effect of load ratio on small crack growth rates was recorded. Fracture surface characterization suggested that the fatigue crack propagation mechanism was a mixture of transgranular and intergranular cracking. Porosity and other material defects played respective important roles in determining the fatigue crack initiation and propagation behavior.