Abstract
Diffusion couples, consisting of sapphire and fused silica, which were annealed in the temperature range from 1678 degrees to 2003 degrees C and analyzed by electron beam microprobe, have provided data on the stable phase equilibrium of the silica-alumina system. Under stable equilibrium conditions, the intermediate compound of this system, mullite (3Al(2)O(3) . 2SiO(2)), melts incongruently at 1828 degrees +/- 10 degrees C and its solid solution field extends from 70.5 to 74.0 percent (by weight) alumina. The stable phase diagram is a composite of the two binary eutectic diagrams: silica-mullite in the absence of alumina and silica-alumina in the absence of mullite. Under metastable conditions, mullite melts congruently at approximately 1890 degrees +/- 10 degrees C and its solid solution field extends to approximately 83.2 percent (by weight) alumina.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.