The shapes of irradiation-produced voids in nickel

Abstract

Voids were produced in nickel by protons and Ni++ ions at 500°C. Methods for an accurate determination and quantitative description of the shape of voids are discussed. The voids thus produced in Ni are prominently cubo-octahedral with 100% truncation, or octahedral with partial {100} truncation, and occasionally cubic with partial {111} truncation. The present results, coupled with previous observations, thus assert a ready change in shape of the voids. Reasons for the wide shape change are explained in terms of the anisotropy of surface energy, the kinetics of growth of void surfaces, and a preferential adsorption of carbon atoms on the {100} surfaces of voids during irradiation. Des cavités ont été produits dans le nickel par irradiation aux protons et aux ions nickel à 500°C. Les méthods pour une détermination exacte et pour une description quantitative de la forme de cavités sont discutées. Les cavités ainsi produits dans le nickel ont éminemment la forme d'octaèdres cubiques avec la troncature complète ou la forme d'octaèdres réguliers tronqués par les plans {100}, et par occasion la forme de cubes tronqués par les plans {111}. Les résultats présents combinés avec les observations précédentes révélent ainsi un changement prompt en forme de cavités. Les raisons pour le large changement de forme sont expliquées en fonction de i'anisotropie d'énergie de surface, de la einétique de croissance de faces de cavités, et d'une absorption préférentiele d'atomes de carbone sur les faces {100} de cavités pendant l'irradiation.