Abstract
The effects of the Achnanthes taeniata and the diatomaceous earth (diatomite) frustules addition on the compressive strength of an epoxy matrix were investigated experimentally. The Achnanthes taeniata frustules having relatively high length/diameter aspect ratio (2-4) were isolated and cultured in laboratory. While the as-received commercial natural diatomite frustules were non-homogenous in shape and size. The filling epoxy matrix with ~6 wt% of commercial natural diatomite increased the compressive strength from 60 MPa to 67 MPa, while the Achnanthes taeniata frustules addition increased to 79 MPa. The increased compressive strength and modulus of the the Achnanthes taeniata frustules filled epoxy was attributed to the higher aspect ratio and relatively strong bonding with the epoxy matrix. The more effective load transfer from the matrix to the Achnanthes taeniata frustules associated with the enhanced interface bonding was also proved microscopically. The frustules were observed to pull-out on the fracture surface of the Achnanthes taeniata frustules filled epoxy.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.