Abstract
A nontrivial polythermal cross-section through the Fe–Ni–S phase diagram was plotted using a combination of directional crystallization and DTA methods. The crystallized sample was grown from the liquid (L) of the following composition Fe = 18, Ni = 35, and S = 47 at.%. It consisted of two single-phase sites formed from mss (Fe z Ni1−z )S1±δ and hzss (Ni z Fe1−z )3±δS2. The phase reaction L + mss = hzss proceeded on the boundary between these sites. The trajectories of melt and solid composition on the Gibbs triangle were calculated from the distribution of components along the sample. The tie-line transformation was determined from these data. Liquidus temperatures along the trajectory were measured by the DTA method and calculated with the help of a mathematical model. The nontrivial cross-section of the diagram constructed from these data shows the phase equilibrium conditions. The cross-section consists of two tie-line linear surfaces L–mss and L–hzss.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.