Abstract
The reaction between solid steel and liquid Al-Zn-Si alloy leads to the formation of a solid intermetallic interfacial layer. In the case of industrial Al-43.5Zn-1.5Si coated steel strips, the thickness of the intermetallic layer is on average 1.35 μm and the kinetics of the reaction is controlled by the effect of Si on Al and Fe diffusivities through the solid intermetallic layer. In this paper it is shown that the thickness of the intermetallic interfacial layer decreases as the Si content in the liquid alloy increases. EDXS microanalysis at the interface of industrial coated steel strips shows that the interfacial intermetallic compounds are chemically similar to those formed in the bulk of Al-43.5Zn-1.5Si liquid baths in continuous coating lines. Differential acid dissolution of the coatings reveals that the intermetallic layer is not planar at the interface with the coating overlay and is formed by grains of different size and chemical composition. Addition of minute quantities of Ti to the Al-Zn-Si liquid alloy causes changes in the morphology of the intermetallic layer and an overall refining of the microstructure.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.