Abstract
The calcium substituted nickel-zinc ferrites with the formula of CaxNi0.75−xZn0.25Fe2O4 (x = 0, 0.25, 0.5 and 0.75) have been prepared by using the chemical co-precipitation method. The X-ray diffraction (XRD) analyses reveal the results that all the samples crystallize in cubic spinel structure and the lattice constants of the samples for x = 0, 0.25, 0.50 and 0.75 are found to be 8.334, 8.348, 8.380 and 8.538 A, respectively. The crystallite size of the samples, obtained from Debye Scherrer’s equation, varies between 12 nm and 27 nm. The scanning electron microscopy (SEM) and energy-dispersive X-ray spectroscopy (EDX) analyses have been conducted to reveal and determine the morphology and stoichiometry of all the prepared CaxNi0.75−xZn0.25Fe2O4 ferrite samples. The SEM images show that the partical sizes for all the samples are at nano size in accordance with the XRD results and EDX results confirm the contents of the produced samples. The dielectric and impedance properties of the prepared ferrite samples have been investigated in the frequency range from 20 Hz to 10 MHz and in the temperature range from 350 to 700 K. The real and imaginary parts of dielectric constant, tan θ, AC and DC conductivity values decrease with increasing calcium content (except x = 0). Contrary to this behavior, real and imaginary parts of impedance increase with increasing calcium content. The general AC conductivity behavior of all samples is like semiconductor behavior. The conductivity mechanism of the sample with x = 0 is explained by the mechanism of correlated barrier hopping (CBH), while it has turned into overlapping large polaron tunneling (OLPT) mechanism for all other samples. From the relaxation time graphs obtained from the impedance data, activation energies of the grain and grain boundaries are obtained. The Nyquist plots are also presented in the temperature range of 350–700 K to determine the conductivity mechanism of the prepared samples and all the plots show only one semi-circle, which means that the dominant transmission comes from the grain boundaries.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: Journal of Materials Science: Materials in Electronics
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.