Abstract
The mechanisms for lithium diffusion in LixCo0.5Ni0.5O2 were investigated using the galvanostatic intermittent titration technique (GITT). Membrane electrodes prepared with poly(vinylidene fluoride) and carbon black were employed in this study. The measured Brunauer–Emmett–Teller (BET) area of the LixCo0.5Ni0.5O2 powder was combined with the GITT data to obtain the lithium chemical diffusion coefficient (ĎLi+), the lithium self-diffusion coefficient (DLi+) and the thermodynamic factor (Φ) as a function of Li concentration (x). All three parameters vary non-monotonically with x. A minimum in ĎLi+ and DLi+ at x=0.5, along with structural changes, suggests the formation of a lithium superlattice at that concentration. The behavior of ĎLi+ is complex but for x<0.34 it eventually undergoes a continuous decrease due to the metallic character of LixCo0.5Ni0.5O2. We attribute the limitation of the specific reversible capacity of LixCo0.5Ni0.5O2 to this decrease in ĎLi+ and to elevated electrode voltages. Li transport in LixCo0.5Ni0.5O2 is analyzed taking the variations in the cell parameters and the oxidation states of the Ni, Co and O ions into account.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.