The Role of Silver in Mitigation of Whisker Formation on Thin Tin Films

Abstract

The mitigating effect of alloying Sn thin films with Ag on the formation of Sn whiskers was investigated by time-resolved investigations employing x-ray diffraction for phase and stress analyses and focused ion beam microscopy for morphological characterization of the surfaces and cross-sections of the specimens. The investigated Sn-6 wt.%Ag thin films were prepared by galvanic co-deposition. The results are compared with those obtained from investigation of pure Sn films and discussed with regard to current whisker-growth models. The simultaneous deposition of Sn and Ag leads to a fine-grained microstructure consisting of columnar and equiaxed grains, i.e. an imperfect columnar Sn film microstructure. Isolated Ag3Sn grains are present at the Sn grain boundaries in the as-deposited films. Pronounced grain growth was observed during aging at room temperature, which provides a global stress relaxation mechanism that prevents Sn whisker growth.