As a fundamental study to develop a new process for producing solar-grade silicon, the effect of granule size on the kinetics of the electrochemical reduction of SiO2 granules in molten CaCl2 was investigated. SiO2 granules with different size ranges were electrolyzed in molten CaCl2 at 1123 K (850 °C). The reduction kinetics was evaluated on the basis of the growth rate of the reduced Si layer and the behavior of the current during electrolysis. The results indicated that finer SiO2 granules are more favorable for a high reduction rate because the contact resistance between the bottom Si plate and the reduced Si particles is small and the diffusion of O2− ions in CaCl2 inside the porous Si shell is easy. Electrolysis using SiO2 granules less than 0.1 mm in size maintained a current density of no less than 0.4 A cm−2 within 20 minutes, indicating that the electrochemical reduction of fine SiO2 granules in molten CaCl2 has the potential of becoming a high-yield production process for solar-grade silicon.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.