Abstract
The tensile, fracture toughness and fatigue properties of Al−Si 319 lost-foam-cast alloy were determined at room temperature. The fatigue properties of this alloy were also determined at 150°C. Fatigue cracks were always initiated at the largest casting pore. Initial pore sizes were measured using a scanning electron microscope. Surface replication showed that majority of the fatigue life was spent in fatigue crack propagation and permitted the estimation of the constants in the Paris power law and the threshold stress intensity factor (ΔK th ). The role of internal casting porosity was quantified using a linear elastic fracture mechanics (LEFM) model for fatigue crack growth. The predicted lives agreed with the measured values within a factor of two.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.