The Relationship of Reaction Temperature, Tg and Rich‐Syndiotacticity of Poly(alkyl methacrylate)s in Modified Microemulsion Polymerization

Abstract

Nanoscale poly(alkyl methacrylate)s including poly(methyl methacrylate), poly(ethyl methacrylate), poly(cyclohexyl methacrylate), poly(iso‐butyl methacrylate) and poly(benzyl methacrylate) were prepared by a modified microemulsion polymerization procedure. NMR analysis suggested that these poly(methacrylate)s samples were higher in syndiotactic content, lower in isotactic content and the glass transition temperatures (Tgs) of them were also higher than those reported in the literature. The tacticities of the poly(methacrylate)s, beside the restricted volume effect of nanoparticles during the modified microemulsion polymerization, were mainly influenced by the reaction temperature, the lower the reaction temperature, the higher the syndiotacticity of the products. The syndiotacticity of the product decreased obviously when the polymerization was carried out at a temperature far above the Tg of the resulting polymer. It was also shown that the tacticity of the polymer was affected by the monomer structure, a monomer with the bulkier alkyl side group would liable to result in a polymer with richer syndiotacticity. Possible mechanism of rich‐syndiotacticity was also discussed.