Abstract
Introduction: The purpose of this study was to evaluate the relationship of modulus of elasticity and micro-hardness of denture bases to pressure transmission under the thermoplastic nylon denture base.Material and Methods: Mandibular first molar acrylic denture teeth (Bioeco) embedded on 15x15x3 mm3 thermoplastic nylon (TCS and BioTone) and poly methyl methacrylate denture bases were evaluated (n=9). A 100N force applied on the specimen using universal testing machine and the pressure transmitted under the specimen observed using pressure transducer. The modulus of the elasticity (n=16) measured on 64x10x3,3 mm3 specimens and micro-hardness (n=16) measured on 10x10x3 mm3 specimens. Data were statistically analyzed using One-way Anova followed by Tukey HSD post hoc test. Pearson correlation test used to evaluate the relationship of modulus of elasticity and micro-hardness on denture bases to pressure transmission (α ≥ 0,05).Results: The results showed that poly methyl methacrylate has the highest pressure transmission compared to others. There was a significant relationship between modulus of elasticity and micro-hardness to pressure transmission under the denture base.Discussion: This study can help dentists to determine the design of dentures, especially in the selection of denture base materials.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: Journal of Biomimetics, Biomaterials and Biomedical Engineering
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.