Abstract
We investigated the thermal behavior of dislocation loops formed in a CH3O-multielement-molecular-ion-implanted epitaxial silicon (Si) wafer by real-time cross-sectional tunneling electron microscopy observation with in situ heating. We found that the CH3O-ion-implantation-induced faulted Frank dislocation loops (FDLs) shrink at a low rate at the beginning of heat treatment (1st stage), and then the shrinkage rate rapidly increased (2nd stage), resulting in the dissolution of the defects. The activation energies for the shrinkage of FDLs in the 1st and 2nd stages were found to be 2.94±0.31 and 4.95±0.25 eV, respectively. The shrinkage behavior in the 1st stage is the desorption of C and O atoms that segregated along the edge of an FDL because of the interaction between the CH3O-ion-implantation-induced FDL and the segregated impurities. On the other hand, the 2nd stage corresponds to the desorption of Si atoms from FDLs and its migration. Our experimental results suggest that thermal stability of the dislocation loop is determined by the kind of segregated impurities around the dislocation loop.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.