Abstract

A dual phase Ti-6A1-4V alloy was tested in uniaxial tension over a large quasi-static loading range (10−5–10−1 s−1) in ambient environment. As strain rate increases, strength of the alloy was found to increase at the expense of ductility. In the low strain-rate region, strain rate sensitivity of the material experienced a gradual decrease during plastic deformation. In the high strain-rate region, strain-rate sensitivity of the material was largely constant for most part of the plastic deformation. The different rate dependent behaviours are believed to be caused by a change of governing plastic deformation mechanism from dislocation slip at low strain rates to twinning at the highest strain rate. Strong fractographic and metallographic evidence was obtained to understand the micromechanisms of plastic deformation.

Full Text
Paper version not known

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.