The processes involved in the Se electrodeposition and dissolution on Au electrode: the H2Se formation

Abstract

The processes involved in the Se electrodeposition, mainly the one related to the formation of H2Se species on Au electrode in perchloric acid solutions, have been investigated through cyclic voltammetry, electrochemical quartz crystal microbalance (EQCM), rotating ring-disc electrode (RRDE), and atomic force microscopy (AFM) techniques. In the experiments performed with the EQCM, with the potential sweep in the negative direction, the responses for the mass variation were divided in three well-defined potential regions: A (from 1.55 to 0.35 V), B (from 0.35 to −0.37 V), and C (from −0.37 to −0.49 V). It was verified that the following processes can occur, respectively: the species (AuO)2H2SeO3 was desorbed during the AuO reduction, the reduction of Se(IV) to Se(0), and the formation of H2Se. When the potential was swept in the positive direction, the responses for the mass variation were divided in four well-defined potential regions: D (from −0.49 to 0.66 V), E (from 0.66 to 0.99 V), F (from 0.99 to 1.26 V), and G (from 1.26 to 1.55 V), and the described processes in these regions were, respectively: the Se deposition and adsorption of water molecules and/or perchlorate ions, the Se dissolution, the Se incorporating mass in the form of HO–Se, and the Au oxidation (all potentials are referred to the Ag/AgCl electrode). Making use of the RRDE, using the collection technique, the formation of H2Se species during the Se electrodeposition was investigated. Therefore, it was confirmed that this species is formed on the disc electrode between −0.3 and −0.55 V vs the Ag/AgCl potential range (collecting the oxidized compound onto the ring electrode). AFM images also indicated that the surface topography of the Se-massive deposit on Au is different from the images registered after the formation of H2Se species, confirming the cathodic stripping of Se.