The Preparation of Ti–Ta Impedance-Graded Coatings with Limited Diffusion by Cold Spraying Combined with Hot Isostatic Pressing

Abstract

Ti–Ta impedance-graded coatings were prepared using cold spraying combined with hot isostatic pressing. Compared to the general Ti–Ta binary diffusion couple, the interdiffusion coefficient of as-sprayed Ti–Ta can be increased by approximately 25 times at 1100 °C due to grain refinement at the interface of the cold-sprayed particles. By the control of interdiffusion, pure Ta and pure Ti regions can remain in the materials after hot isostatic pressing at 900 °C. Hot isostatic pressing with capsulate reduced the porosity of the material efficiently to less than 0.02%. The strength of the as-sprayed Ti–Ta composite coating was significantly improved to 990.1 MPa, and the fracture strain reached 11.5%. The strengthening mechanism of Ti–Ta composite coatings relies primarily on the hindrance of dislocation slip by phase interfaces between α and β. Moreover, the macroscopic interfacial bonding strength of the graded material exceeds 881 MPa, which is comparable to that of bulk materials.