Abstract
Electron Spin Resonance (ESR) has recently been very successfully applied to the problem of thermal oxide — Si interfaces1–3. That work resulted in the identification of the Pb center as the primary fast interface trap and the determination that its basic structure is a trivalent Si atom at the Si-SiO2 interface. In addition to the technological motivations, there is also fundamental interest in this defect, which is at the interface between a crystalline solid and an amorphous one, and, therefore, might be expected to have features characteristic of defects in both types of materials. The detailed ESR study of the structure of this defect is inhibited by the small fraction of interfacial atoms in a typical Si-SiO2 structure. It has recently been shown that the principal paramagnetic defect observed in silicon on insulator materials formed by oxygen implantation is a Pb center at the interface between Si and SiO2 precipitates in the Si film over the buried oxide layer4–6. The total precipitate surface area can be much greater than the simple surface area of an Si-SiO2 structure. This increased number of “interfacial” atoms affords the opportunity to conduct more detailed ESR studies of the Pb center than readily possible with Si-thermal oxide structures. In addition these interfaces are formed in a significantly different manner than the thermal oxide interfaces and a comparison of the Pb centers formed in the two manners may offer insights into their formation.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.