Abstract
AbstractThe effect of partial replacement of silica or calcium carbonate (CaCO3) by halloysite nanotubes (HNTs) on the curing behavior, tensile properties, dynamic mechanical properties, and morphological characteristics of ethylene propylene diene monomer (EPDM) composites was studied. Five different compositions of EPDM/Silica/HNT and EPDM/CaCO3/HNT compounds (i.e. 100/30/0, 100/25/5, 100/15/15, 100/5/25, and 100/0/30 parts per hundred rubber (phr)) were prepared on a two‐roll mill. The results indicated that the replacement of CaCO3 by HNTs increased the tensile strength, elongation at break (Eb), and tensile modulus of composites from 0 to 30 phr of HNTs whereas for silica, the maximum tensile strength and Eb occurred at 5 phr loading of HNTs with an enhanced stress at 300% elongation (M300). The curing results show that, with replacement of silica or CaCO3 by HNTs, the cure time (t90) and cure rate (CRI) were decreased and increased, respectively. Scanning electron microscopy investigation confirmed that co‐incorporation of 5 phr of HNTs with silica would improve the dispersion of silica and enhanced the interactions between fillers and EPDM matrix. © 2009 Wiley Periodicals, Inc. J Appl Polym Sci, 2009
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.