Abstract
The oxidation of Cu particles supported on oxidised Si(100) by molecular oxygen was investigated by means of ellipsometry and Nuclear Reaction Analysis. Stepwise oxidation of a sample containing 15 nm Cu particles at 473 K and 0.1 Pa showed that the sample was eventually oxidised to CuO 0.74 ± 0.08, which is very close to CuO 0.67, known from the literature. The ellipsometric parameter δΔ followed a highly non-linear curve upon oxygen exposure, exhibiting a maximum during oxidation, but stabilising when the CuO 0.74 ± 0.08 oxide composition was reached. The oxide stoichiometry was less than Cu 2O at the maximum of the δΔ-curve, indicating that the CuO 0.67-phase nucleated in the sample before the formation of Cu 2O had been completed. During surface oxidation, the sensitivity of δΔ to the amount of oxygen was similar to that of copper single crystals. The sensitivity of δΔ to oxygen increased significantly while samples were oxidised to Cu 2O and further: it was almost three times larger than the sensitivity of δΔ to oxygen for surface oxidation.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.