THE OPTIMIZATION OF PRODUCTION ZEOLITE Y CATALYST FROM RHA BY RESPONSE SURFACE METHODOLOGY

Abstract

Rice husk is the milling byproduct of rice and is a major waste product of the agriculture industry. Amorphous silica, commonly referred to as rice husk ash, was extracted from rice husk by acid leaching, pyrolysis, and carbon-removing processes. These properties make the ash a valuable raw material for many industries. This paper is study of synthesized of zeolite Y from rice husk ash. Zeolite Y synthesis is used for petroleum industry as expensive catalyst. Rice husk was calcined at temperature 700 o C for two hours using furnace to produce pure silica. The composition of synthesized of zeolite Y from rice husk was 2.24 Na 2 O:Al 2 O 3 :8SiO 2 :112 H 2 O. The gel solution was mixed at room temperature for 24 hours using autoclave. Then, the gel solution was heated with variable temperature and time crystallization. The product zeolite synthesis Y was filtered and washed with distilled water until pH lower than ten, than dried at oven. This product was analyzed with X-Ray Diffraction (XRD). From XRD analyze result indicated that from rice husk ash can produced zeolite synthesis Y which high crystallization degree. The optimum conditions for synthesis of zeolite Y from rice husk ash are temperature at 100 o C for 48 hours, silicate at 20%, and aluminate at 10%.