Abstract
The purpose of this work is to provide a novel perspective for investigating the damage of diamond surfaces implanted by MeV phosphorus (P) ions and recovery of the surfaces after high-temperature annealing. SRIM simulation and low-temperature luminescence spectroscopy were performed to analyze the properties of the samples comprehensively. The results revealed that a certain degree of diamond lattice damage was caused without graphitization by the irradiation of 1 MeV P ions with a fluence value of 1015 ions/cm2. The SRIM simulation revealed that the ions that were implanted into the lattice collided with carbon atoms. These ions stopped at a depth of approximately 0.55 μm and generated intrinsic diamond defects on the diamond near the surface. The simulated defects were confirmed by the appearance of neutral single vacancy (GR1) centers in the photoluminescence (PL) spectrum after annealing at 400 °C. In addition, the annealing behavior of optical centers at 900 °C indicated significant damage recovery, including the disappearance of GR1 centers, combined with the increased intensity, slightly blue-shifted peak position, and narrowed FWHM of the nitrogen-vacancy (NV) center.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.